Quick Setting Agent

Delivery term:The date of payment from buyers deliver within days
  • Price:

    Negotiable

  • minimum:

  • Total supply:

  • Delivery term:

    The date of payment from buyers deliver within days

  • seat:

    Chongqing

  • Validity to:

    Long-term effective

  • Last update:

    2019-11-16 01:00

  • Browse the number:

    79

Send an inquiries
Company Profile
Chongqing Borida Construction Materials Co.,Ltd
By certification [File Integrity]
Contact:

cqbrd888(Mr.)  

Email:

Telephone:

Phone:

Area:

Chongqing

Address:

Baisha Industrial Park, Jiangjin District, Chongqing

Website: http://www.cqbrd.net/ http://cqbrd888.21134653.com/
Product details
Technical performance comparison

Contrast item

Alkali content

Content

1d strength

Late strength

Durability

alkali-free

0-0.3%

6-8%

increase

10-15MPa

increase

10-20%

Than the base concrete shrinkage 1 times, alkali-free aggregate reaction hazards.

The impermeability of concrete is higher than that of alkaline set accelerator.

alkali

10-20%

3-5%

reduce

8-15MPa

reduce

25-35%

1.5-2 times larger than the base concrete shrinkage, alkali aggregate reaction occurs at any time.

The impermeability of concrete is lower than that of alkali-free set accelerator.


In conclusion

1. The content of alkaline quick-setting agent is lower than that of alkali-free set accelerator.

2. Alkaline quick-setting agent early strength slightly higher than the alkali-free set accelerator.

3. The strength of alkaline set accelerator is about 50% lower than that of alkali-free set accelerator. Thus, in the design of the same reference to the injection of concrete, the alkaline set accelerator needs to increase the amount of cement, alkali-free set accelerator can reduce the amount of cement.

4. The durability of alkali-free set accelerator is much higher than that of alkaline quick-setting agents. The alkaline set accelerator because of its high alkali content, when the active aggregate encountered, it will cause alkali aggregate reaction. After the occurrence of alkali aggregate reaction of the shotcrete, the structure becomes loose, loss of tunnel support capacity, serious may cause tunnel collapse. The alkali-free set accelerator has little alkali content and does not cause an alkali aggregate reaction. In addition, the shrinkage performance of alkali-free set accelerator is higher than that of alkaline set accelerator.